410/430 stainless steel wire mesh raw material material introduction and characteristics

410/430 stainless steel wire mesh raw material material introduction and characteristics introduction
1. Uncommon stainless steel wire mesh material: 410 stainless steel 
410, it belongs to martensitic stainless steel, used after quenching and tempering, its strength, plasticity and toughness are well matched. It has good corrosion resistance in weak corrosive media with a temperature not exceeding 30°C; it has sufficient corrosion resistance in fresh water, steam and humid atmosphere; it has stable oxidation resistance below 700°C. In order to improve the wear resistance, corrosion resistance and fatigue resistance of parts, carbonitriding or nitriding treatment can be carried out. In the annealed state, it has high plasticity and can be cold-pressed by deep rolling, stamping, bending and curling; it has good welding and mechanical cutting processability and can be polished. It is mainly used to manufacture parts that require medium strength and high toughness under the action of corrosive media and impact loads. 
410 Chemical composition: Carbon (C): ≤0.15 Silicon (Si): ≤1.00 Manganese (Mn): ≤1.00 Phosphorus (P): ≤0.035 Sulfur (S): ≤0.030 Nickel (Ni): 0 Chromium (Cr): 11.5--13.5 Molybdenum (Mo): 0 

2. Uncommon stainless steel wire mesh material: 430 stainless steel 
430 stainless steel is a general steel with good corrosion resistance, better thermal conductivity than austenite, smaller thermal expansion coefficient than austenite, heat fatigue resistance, addition of stabilizing element titanium, good mechanical properties of weld parts. 430 stainless steel is used for architectural decoration, fuel burner parts, household appliances, and home appliance parts. 430F is a steel with easy-to-cut properties added to 430 steel, mainly used for automatic lathes, bolts and nuts, etc. 430LX adds Ti or Nb to 430 steel, reduces C content, and improves processing performance and welding performance.