1cr25ni20si2 stainless steel wire mesh Introduction to Characteristics and Applications
2024-07-29 16:24:12
wiremeshxr
1cr25ni20si2 stainless steel wire mesh is also known as 1cr25ni20si2 stainless steel screen, 1cr25ni20si2 stainless steel filter, 1cr25ni20si2 stainless steel mesh, 1cr25ni20si2 stainless steel woven mesh, 1cr25ni20si2 stainless steel square hole mesh.
1cr25ni20si2 is a high temperature resistant austenitic stainless steel, 310S is the American designation, it is a chromium-nickel stainless steel with better high temperature resistance and can withstand temperatures above 1150 degrees.
1Cr25Ni20Si2 belongs to the national standard austenitic heat-resistant steel, implementation standard: GB /T 1221-2007
1Cr25Ni20Si2 corresponding grades: 1. National standard GB-T standard: digital grade: S38340, new grade: 16Cr25Ni20Si2, old grade: 1Cr25Ni20Si2, 2. American standard: ASTMA standard: one, SAE standard: one, UNS standard: one, 3. Japanese standard JIS standard: 314, 4. German standard DIN standard: 1.4841, 5. European standard EN standard: X8CrNiSI25-21, French standard NF standard: /, British standard BS standard: /, Swedish: /NTR standard: -.
1Cr25Ni20Si2 has high high temperature strength and oxidation resistance, is sensitive to sulfur-containing atmosphere, and has a tendency to embrittle the precipitation phase at 600-800°C. It is suitable for making various furnace components that bear stress.
1Cr25Ni20Si2 heat treatment specification: solid solution at 1080-1130℃ and rapid cooling.
1Cr25Ni20Si2 metallographic structure: The organizational characteristics are austenite.
1Cr25Ni20Si2 tensile strengthσb (MPa): ≥590
1Cr25Ni20Si2 conditional yield strength σ0.2 (MPa): ≥295
1Cr25Ni20Si2 elongation δ5 (%): ≥35
1Cr25Ni20Si2 Sectional shrinkage ψ (%): ≥50
1Cr25Ni20Si2 Hardness: ≤187HB
Chemical composition of 1Cr25Ni20Si2: ⑴ Carbon C: ≤0.20, ⑵ Silicon Si: 1.50~2.50, ⑶ Manganese Mn: ≤1.50, ⑷ Phosphorus P: ≤0.040, ⑸ Sulfur S: ≤0.030, ⑹ Chromium Cr: 24.00~27.00, ⑺ Nickel Ni: 18.00~21.00.
1Cr25Ni20Si2 physical properties: ⑩Magnetic properties: None.
1Cr25Ni20Si2 properties: ⑴ Delivery status: bar solution treatment, plate solution pickling, ⑵ Tensile strength (RM/MPa): 520, ⑶ Elongation strength (Rp0.2/MPa): 205, ⑷ Elongation A/%: 40, ⑸ Section shrinkage (Z/%): 50
1Cr25Ni20Si2 heat treatment: ①Hardness HBW≤: solid solution 187, hardness HRB≤: 90, ②Heating temperature: 1080~1130, ③Heating method: fast cooling
1Cr25Ni20Si2 application areas: suitable for making various furnace components that bear stress.
Made in China Mao Qun stainless steel wire mesh, stainless steel screen mesh, stainless steel woven mesh, nickel alloy wire mesh, copper wire mesh, screen mesh,GFW metal wire mesh,Stainless steel wire mesh,Alloy wire mesh,Knitted metal wire mesh,Woven Wire Mesh,Structured packing