Customers often ask this question when consulting on purchasing stainless steel screens. Now we will solve this problem for you! Ordinary stainless steel plates can withstand high temperatures of at least 500 degrees. Stainless steel plates have many excellent properties, exquisite appearance, long service life, and can be 100% recycled, so they are widely used.

Commonly used high temperature resistant stainless steel grades include: materials: 304, 304L, 316L, 347, 316Ti, 317, 317L, 321, 310S, S31803, 904L, 330, 309S, 310S, 2205, etc., as well as ferrite (409/409L, 410, 430, 436/436L, 439/439L, 444) and other common steel grades and some special steel grades.
High temperature stainless steel refers to heat-resistant stainless steel, such as 309S and 310S in stainless steel. 309S can reach a maximum working temperature of 1100 degrees, and 310S can reach a maximum working temperature of 1200 degrees.
However, many high temperature materials are not stainless steel, such as 2080 (Cr20Ni80), 1560 (Cr15Ni60), etc. Usually many people regard these high-temperature materials as stainless steel, but in fact they are nickel-based alloys among high-temperature alloys.

The three major standards for stainless steel plates are: national standard GB 24511-2009, American standard ASTM SA240/240M, European standard EN10028.-1, 7 2007 standard mainly stipulates the grade, chemical composition, size and shape of the steel plate, the performance and test of the stainless steel plate. High temperature resistant stainless steel screen is often used in boiler manufacturing, steam turbines, industrial furnaces, and parts working at high temperatures in aviation, power plants, petrochemical and other industrial sectors.
Stainless steel 310S (0Cr25Ni20/0Cr25Ni20Si2), heat-resistant stainless steel screen, domestic grade 0Cr25Ni20, American grade 310S, also known as 2520, is used in the manufacture of high temperature resistant furnace tubes. Chemical composition of 310S (%): Ni Nickel: 19.00-22.00Cr Chromium; 24.00-26.00Si is austenitic chromium-nickel stainless steel with good oxidation resistance,
     310S (0Cr25Ni20) stainless steel plate is the most heat-resistant, also called 2520 stainless steel plate; it can withstand temperatures of at least 1000 degrees without any problems, you can use it under harsh conditions, and it has excellent work hardening (non-magnetic); 310S is a good oxidation resistance, corrosion resistance, and high temperature resistance. Because of the higher percentage of chromium and nickel, 310S has good creep strength, can continue to work at high temperatures, and has good high temperature resistance.
     316 stainless steel plate has a temperature resistance of about 800 degrees Celsius, which is also relatively high. Because 316 adds MO, its corrosion resistance, atmospheric corrosion resistance and high temperature strength are also relatively good.
     304 stainless steel plate can withstand temperatures of about 500°C, and the performance is extremely deteriorated
     . 321 stainless steel plate has high temperature resistance and corrosion resistance. Due to the higher percentage of chromium and nickel, 310s has much better creep strength, can continue to work at high temperatures, and has good high temperature resistance.
By comparing the heat resistance temperatures of several commonly used stainless steel materials, it can be seen that 310S stainless steel is the most resistant to high temperatures.