06Cr18Ni11Ti stainless steel wire mesh application, grade, chemical composition, characteristics

06Cr18Ni11Ti stainless steel wire mesh application, brand, chemical composition, characteristics
06Cr18Ni11Ti is the new brand of TP321, and the old brand of TP321 is 0Cr18Ni10Ti.
Brief history of structural development Production process Application field
China's stainless steel brands are composed of chemical composition plus numbers, but it is not easy to remember.
So we usually call them American brands and Japanese brands, which are composed of numbers plus letters.
0Cr18Ni10Ti chemical composition:
Carbon C: ≤0.08
Silicon Si: ≤1.00
Manganese Mn: ≤2.00
Sulfur S: ≤0.030
Phosphorus P: ≤0.035
Chromium Cr: 17.00～19.00
Nickel Ni: 9.00～12.00
Titanium Ti: =5x(c%-0.02)~0.8 Mechanical
properties
Tensile strength σb (MPa): ≥520Conditional
yield strength σ0.2 (MPa): ≥205Elongation
δ5 (%): ≥40Sectional
reduction ψ (%): ≥50Hardness
: ≤187HB; ≤90HRB; ≤200HV
06Cr18Ni11Ti chemical composition: TP321 new and old brands have the same chemical composition, 06Cr18Ni11Ti and 0Cr18Ni10Ti can replace each other.
Stainless steel 0Cr18Ni11Ti is a corrosion-resistant steel with excellent resistance to intergranular corrosion and high strength after cold working.
Product features: excellent processability, weldability, impact strength, good atmospheric corrosion resistance and many organic and inorganic chemical corrosion. Its performance is very similar to 304. Due to the addition of titanium, the formation of chromium carbide is effectively controlled, making it have better resistance to intergranular corrosion and high temperature strength. 321 stainless steel has good resistance to high temperature stress fracture and high temperature creep. Suitable for use at 900℃.
0Cr18Ni10Ti is a kind of stainless steel. It adds Ti elements to 304 steel to prevent intergranular corrosion; it is suitable for use at 430℃~900℃. It is used in aircraft, exhaust pipes, boiler drums, etc.